Underlayment Self Leveling Compound for Residential Application of Vinyl Flooring Timber Flooring

• Customization: Available
• Application: Commercial Construction, Decorative Concrete, Residential Construction
• Color: Gray
• Model NO.: K50
• Setting Time: Fast-Setting
• Special Additives: Fiber-Reinforced, Shrinkage-Reducing
• Type: High-Strength Concrete
• Dry Powder Density: About 1.3kg\L
• Time Before Covering: About 24-48 Hours
• Fire Resistance Rating: A1
• Mixing Ratio: Cement(25kg) : Water(6.5L - 7L)
• Compressive Strength: 23-25MPa After 28 Days
• Flexural Strength: >7MPa After 28 Days
• Transport Package: Wood Case
• Specification: 20kg/bag
• Trademark: Lan Guan
• Origin: China
• Package Size: 50.00cm * 30.00cm * 35.00cm
• Package Gross Weight: 65.000kg
• Lead Time: 3 days (1 - 3 Bags) ; To be negotiated ( > 3 Bags)

Product Description

 

Product introduction

 

Lan Guan K50 Commercial Self-Leveling Cement is a highly formulatedhydraulic hardening inorganic composite

material. It can be used for leveling indoor floors before the installation of vinyl flooring, sheet materials, and wooden

flooring. It's applied on solid substrates such as concrete floors, cement mortar screeds, and stone tile surfaces.

 

Application scope

Suitable for indoor areas as a leveling layer before installing PVC flooring, LVT (Luxury Vinyl Tile) flooring, carpet,

and SPC (Stone Plastic Composite) flooring. It is particularly suitable as a leveling layer for indoor floor decoration

where the surface needs to be covered with other decorative materials. This self-leveling compound is a base layer

material. The application thickness should not be less than 2mm and not exceed 8mm.
 

Performance characteristics

 

>> Excellent flowability, automatically leveling of the floor.

>> Improves the density, hardness, and homogeneity of the substrate.

>> Reduces substrate porosity and enhances uniform absorption.

>> Fast-setting and early strength, allowing for sanding and laying of decorative floor materials within 1-2 days.

>> Low shrinkage, preventing floor cracking.

 

Mixing Ratio	25kg cent : 6.3L~ 6.5L water
Dry power density	about 1.3kg\L
Time before covering	about 24-48 hours
Consumption	1.7kg\m\mm2
Compressive strength	about 6Map after 1 day about 23 - 25mpa after 28 days
Flexural strength	> 2Map after 1 day > 7Map after 28 days
Fire Rating Level	A1