Versatile Flooring Leveling Material for Enhanced Floor Stability

• Customization: Available
• Application: Commercial Construction, Decorative Concrete, Residential Construction
• Color: Gray
• Model NO.: K50
• Setting Time: Fast-Setting
• Special Additives: Fiber-Reinforced, Shrinkage-Reducing
• Type: High-Strength Concrete
• Dry Powder Density: About 1.3kg\L
• Time Before Covering: About 24-48 Hours
• Fire Resistance Rating: A1
• Mixing Ratio: Cement(25kg) : Water(6.5L - 7L)
• Consumption: 1.7kg\M\mm2
• Compressive Strength: 23-25MPa After 28 Days
• Flexural Strength: >7MPa After 28 Days
• Transport Package: Wood Case
• Specification: 25kg/bag
• Trademark: Lan Guan
• Origin: China
• Package Size: 40.00cm * 25.00cm * 11.00cm
• Package Gross Weight: 25.000kg

Product Description

Product introduction

 

Lan Guan K50 Commercial Self-Leveling Cement is a meticulously engineered hydraulic hardening inorganic composite.

This premium material is ideal for expertly leveling indoor floors, providing a flawless foundation for your luxurious vinyl, sheet materials, and wooden flooring installations.

It is designed to be seamlessly applied over sturdy substrates like concrete floors, cement mortar screeds, and stone tile surfaces.

 

Application scope

Engineered to meet the demands of indoor spaces, this versatile leveling layer is perfect for preparing surfaces before the installation of PVC flooring, LVT (Luxury Vinyl Tile) flooring, carpets,

and SPC (Stone Plastic Composite) flooring. Its advanced formulation makes it especially suitable as a leveling layer for any decorative indoor floor installations,

where the surface requires coverage with other elegant decorative materials. This self-leveling compound serves as the essential base layer,

ensuring the application thickness ranges from a minimum of 2mm to a maximum of 8mm, thus achieving optimum leveling results.

Performance characteristics

 

>> Exceptional flowability, ensuring the floor self-levels with precision.

>> Significantly enhances substrate density, hardness, and uniformity, creating a solid foundation.

>> Diminishes substrate porosity and boosts uniform absorption rates, ensuring consistent results.

>> Rapid setting and early strength development, allowing for the swift sanding and installation of decorative floor materials within just 1-2 days, maximizing efficiency.

>> Minimal shrinkage, expertly preventing floor cracking and maintaining structural integrity.

Mixing Ratio	25kg cent : 6.3L~ 6.5L water
Dry power density	about 1.3kg\L
Time before covering	about 24-48 hours
Consumption	1.7kg\m\mm2
Compressive strength	about 6Map after 1 day about 23 - 25mpa after 28 days
Flexural strength	> 2Map after 1 day > 7Map after 28 days
Fire Rating Level	A1