Superior Self-Leveling Compound for Wooden Floor Renovation Needs

• Customization: Available
• Application: Commercial Construction, Decorative Concrete, Residential Construction
• Color: Gray
• Model NO.: K20
• Special Additives: Fiber-Reinforced, Shrinkage-Reducing
• Type: High-Strength Concrete
• Mixing Ratio: Cement Vs Water: 25kg Vs 6.3L~ 6.5L
• Dry Powder Density: About 1.3kg\L
• Time Before Covering: About 24-48 Hours
• Consumption: 1.7kg/M2/mm
• Compressive Strength: About 18-20MPa After 28 Days
• Flexural Strength: >5MPa After 28 Days
• Fire Resistance: A1
• Transport Package: Wood Case
• Specification: 25kg/bag
• Trademark: Lan Guan
• Origin: China

Product Description

Product introduction

Lan Guan K20 Self-Leveling Cement for Wooden Flooring is a premier foundational floor leveling material, meticulously formulated with special cement, precision fine aggregates, premium polymer spray-dried powder resin from prestigious foreign brands, and a blend of advanced cement additives.

The innovative formula incorporates wood fibers, significantly enhancing the crack resistance of the self-leveling cement, achieving strength levels of over 18-20 MPa. This product boasts exceptional fluidity and high plasticity, making it ideal for leveling floors in residential wooden flooring applications.

Application scope

Perfect for rapid floor leveling in residential decorations, office spaces, and public areas (such as shopping malls, supermarkets, schools, hospitals, and other public venues). The surface is optimal for laying various types of wooden flooring, SPC flooring, carpets, ceramic tiles, stone tiles, and stone slabs. It is compatible with adhesives for wooden

flooring and adhesives for ceramic tiles and stone materials. Application thickness ranges from 3mm to 40mm. For thicknesses exceeding 40mm, adding 50% coarse sand aggregate (particle size 3-10mm) is recommended. This product is engineered with low shrinkage properties to ensure it will not crack or become hollow.

 

Performance characteristics

>> High-fluidity material with exceptional self-leveling performance

>> Micro-expansion system, no shrinkage, and quick-drying

>> Outstanding crack resistance, suitable for thicknesses from 3mm to 3cm

>> Moisture-proof and resistant to toxicity, significantly extending the

service life of the floor

>> Eco-friendly material, with no release of toxic or harmful gases

Mixing ratio	25kg cement : 6.3L~ 6.5L water
Dry powder density	about 1.3kg\L
Time before covering	about 24-48 hours
Consumption	1.7kg\m \mm2
Compresslve strength	about 6Map after 1 day about 18-20mpa after 28 days
Folding strength	about 2Map after 1 day about 5Map after 28 days
Fire resistance rating	A1