Easy-Mix Self-Leveling Cement for Wooden Floor Preparation Needs

• Customization: Available
• Application: Commercial Construction, Decorative Concrete, Residential Construction
• Color: Gray
• Model NO.: K20
• Special Additives: Fiber-Reinforced, Shrinkage-Reducing
• Type: High-Strength Concrete
• Mixing Ratio: Cement Vs Water: 25kg Vs 6.3L~ 6.5L
• Dry Powder Density: About 1.3kg\L
• Time Before Covering: About 24-48 Hours
• Consumption: 1.7kg/M2/mm
• Compressive Strength: About 18-20MPa After 28 Days
• Flexural Strength: >5MPa After 28 Days
• Fire Resistance: A1
• Transport Package: Wood Case
• Specification: 25kg/bag
• Trademark: Lan Guan
• Origin: China

Product Description

Product introduction

Lan Guan K20 Self-Leveling Cement for Wooden Flooring serves as the ultimate foundational floor leveling material, meticulously engineered with premium special cement, refined fine aggregates, imported polymer spray-dried powder resin, and other innovative cement additives.

This advanced formula includes wood fibers, significantly boosting the crack resistance of the self-leveling cement, achieving a robust strength exceeding 18-20 MPa. It boasts exceptional fluidity and plasticity, making it perfect for leveling residential wooden flooring with unparalleled ease and reliability.

Application scope

Ideal for rapid floor leveling in residential decorations, office environments, and public spaces (including shopping malls, supermarkets, educational institutions, hospitals, and other communal areas). The surface is well-suited for diverse flooring options such as wooden flooring, SPC flooring, carpets, ceramic tiles, stone tiles, and stone slabs. It is compatible with adhesives for wooden

flooring and those for ceramic tiles and stone materials. The application thickness ranges from 3mm to 40mm. For thicknesses beyond 40mm, incorporating 50% coarse sand aggregate (particle size 3-10mm) is recommended. This product features minimal shrinkage, ensuring it will not crack or become hollow.

 

Performance characteristics

>> Remarkable high-fluidity material with outstanding self-leveling capabilities

>> Incorporates a micro-expansion system, ensuring no shrinkage and quick drying

>> Superior crack resistance, effective thickness applicability ranging from 3mm to 3cm

>> Moisture-proof and toxin-resistant properties, which enhance the

longevity of the flooring

>> Eco-friendly composition, free from toxic or harmful gas emissions

Mixing ratio	25kg cement : 6.3L~ 6.5L water
Dry powder density	about 1.3kg\L
Time before covering	about 24-48 hours
Consumption	1.7kg\m \mm2
Compresslve strength	about 6Map after 1 day about 18-20mpa after 28 days
Folding strength	about 2Map after 1 day about 5Map after 28 days
Fire resistance rating	A1