Innovative Floor Preparation Cement for Quick Wooden Floor Projects

• Customization: Available
• Application: Commercial Construction, Decorative Concrete, Residential Construction
• Color: Gray
• Model NO.: K20
• Special Additives: Fiber-Reinforced, Shrinkage-Reducing
• Type: High-Strength Concrete
• Mixing Ratio: Cement Vs Water: 25kg Vs 6.3L~ 6.5L
• Dry Powder Density: About 1.3kg\L
• Time Before Covering: About 24-48 Hours
• Consumption: 1.7kg/M2/mm
• Compressive Strength: About 18-20MPa After 28 Days
• Flexural Strength: >5MPa After 28 Days
• Fire Resistance: A1
• Transport Package: Wood Case
• Specification: 25kg/bag
• Trademark: Lan Guan
• Origin: China

Product Description

Product introduction

Lan Guan K20 Self-Leveling Cement for Wooden Flooring is a premium foundational floor leveling material. Expertly formulated with special cement, high-quality fine aggregates, advanced polymer spray-dried powder resin from leading international brands, and cutting-edge cement additives.

The innovative formula incorporates wood fibers, significantly enhancing the crack resistance of the self-leveling cement, with strength reaching a robust 18-20 MPa. Boasting high fluidity and exceptional plasticity, it is perfectly suited for leveling floors in residential wooden flooring applications, ensuring a flawless foundation.

Application scope

Ideal for rapid floor leveling in residential decorations, office spaces, and public areas such as shopping malls, supermarkets, schools, hospitals, and other high-traffic public places. The surface is ideal for laying a wide variety of wooden flooring, SPC flooring, carpets, ceramic tiles, stone tiles, and stone slabs. It is compatible with adhesives for wooden

flooring as well as adhesives for ceramic tiles and stone materials. Application thickness ranges from 3mm to a substantial 40mm. For thicknesses exceeding 40mm, it is recommended to add 50% coarse sand aggregate (particle size 3-10mm). This product boasts low shrinkage, ensuring it will not crack or become hollow.

 

Performance characteristics

>> High-fluidity material offering superior self-leveling performance.

>> Micro-expansion system ensures no shrinkage and quick-drying capabilities.

>> Excellent crack resistance with applicable thickness from 3mm to 3cm.

>> Moisture-proof and resistant to toxicity, significantly extending the

service life of the floor.

>> Environmentally friendly material, with no release of toxic or harmful gases.

Mixing ratio	25kg cement : 6.3L~ 6.5L water
Dry powder density	about 1.3kg\L
Time before covering	about 24-48 hours
Consumption	1.7kg\m \mm2
Compresslve strength	about 6Map after 1 day about 18-20mpa after 28 days
Folding strength	about 2Map after 1 day about 5Map after 28 days
Fire resistance rating	A1