Reliable Floor Leveling Material for Quick Wooden Floor Enhancements

• Customization: Available
• Application: Commercial Construction, Decorative Concrete, Residential Construction
• Color: Gray
• Model NO.: K20
• Special Additives: Fiber-Reinforced, Shrinkage-Reducing
• Type: High-Strength Concrete
• Mixing Ratio: Cement Vs Water: 25kg Vs 6.3L~ 6.5L
• Dry Powder Density: About 1.3kg\L
• Time Before Covering: About 24-48 Hours
• Consumption: 1.7kg/M2/mm
• Compressive Strength: About 18-20MPa After 28 Days
• Flexural Strength: >5MPa After 28 Days
• Fire Resistance: A1
• Transport Package: Wood Case
• Specification: 25kg/bag
• Trademark: Lan Guan
• Origin: China

Product Description

Product introduction

Lan Guan K20 Self-Leveling Cement for Wooden Flooring, a premier foundational floor leveling material, is specifically formulated with high-quality special cement, meticulously selected fine aggregates, premium polymer spray-dried powder resin sourced from renowned foreign brands, and a blend of other advanced cement additives.

The innovative formula includes robust wood fibers, significantly enhancing the crack resistance of the self-leveling cement, with impressive strength reaching over 18-20 MPa. Boasting high fluidity and exceptional plasticity, it is perfectly suited for leveling floors in residential wooden flooring applications, ensuring a flawless finish.

Application scope

Ideal for rapid floor leveling in residential decoration, office spaces, and public areas (such as shopping malls, supermarkets, schools, hospitals, and various other public venues). The surface is adeptly prepared for laying multiple types of wooden flooring, SPC flooring, carpets, ceramic tiles, stone tiles, and stone slabs. It seamlessly integrates with adhesives for wooden

flooring as well as adhesives for ceramic tiles and stone materials. Suitable application thickness ranges from 3mm to 40mm. For thicknesses exceeding 40mm, it is recommended to add 50% coarse sand aggregate (particle size 3-10mm) to the mixture. This product is designed to have low shrinkage, ensuring it will not crack or become hollow over time.

 

Performance characteristics

>> Highly fluid material with outstanding self-leveling capabilities

>> Innovative micro-expansion system ensures no shrinkage and rapid drying

>> Superior crack resistance, suitable for application thicknesses from 3mm to 3cm

>> Moisture-proof and non-toxic, extending the service life of the floor

>> Eco-friendly composition, guaranteeing no release of toxic or harmful gases

>> Environmentally friendly material, no release of toxic or harmful gas

Mixing ratio	25kg cement : 6.3L~ 6.5L water
Dry powder density	about 1.3kg\L
Time before covering	about 24-48 hours
Consumption	1.7kg\m \mm2
Compresslve strength	about 6Map after 1 day about 18-20mpa after 28 days
Folding strength	about 2Map after 1 day about 5Map after 28 days
Fire resistance rating	A1