Efficient Self-Leveling Compound for Wooden Floor Renovation Solutions

• Customization: Available
• Application: Commercial Construction, Decorative Concrete, Residential Construction
• Color: Gray
• Model NO.: K20
• Special Additives: Fiber-Reinforced, Shrinkage-Reducing
• Type: High-Strength Concrete
• Mixing Ratio: Cement Vs Water: 25kg Vs 6.3L~ 6.5L
• Dry Powder Density: About 1.3kg\L
• Time Before Covering: About 24-48 Hours
• Consumption: 1.7kg/M2/mm
• Compressive Strength: About 18-20MPa After 28 Days
• Flexural Strength: >5MPa After 28 Days
• Fire Resistance: A1
• Transport Package: Wood Case
• Specification: 25kg/bag
• Trademark: Lan Guan
• Origin: China

Product Description

Product introduction

Lan Guan K20 Self-Leveling Cement for Wooden Flooring is an advanced foundational floor leveling material. Expertly formulated with premium special cement, fine aggregates, top-tier polymer spray-dried powder resin sourced from renowned foreign brands, and an array of specialized cement additives.

This innovative formula includes wood fibers, significantly enhancing the crack resistance of the self-leveling cement, with strength reaching an impressive 18-20 MPa. It boasts high fluidity and superior plasticity, making it ideal for leveling floors in residential wooden flooring applications.

Application scope

Perfectly suited for rapid floor leveling in residential decorations, office spaces, and a variety of public areas (including shopping malls, supermarkets, schools, hospitals, and other public venues). The surface is primed for laying various types of wooden flooring, SPC flooring, carpets, ceramic tiles, stone tiles, and stone slabs. It is compatible with adhesives for wooden

flooring and adhesives for ceramic tiles and stone materials. The application thickness ranges from 3mm to 40mm. For thicknesses exceeding 40mm, 50% coarse sand aggregate (particle size 3-10mm) should be added. This product features low shrinkage, ensuring it will not crack or become hollow.

 

Performance characteristics

>> High-fluidity material with exceptional self-leveling performance

>> Micro-expansion system, no shrinkage, and quick-drying properties

>> Superior crack resistance, suitable for thicknesses from 3mm to 3cm

>> Moisture-proof and non-toxic, contributing to an extended

service life of the floor

>> Environmentally friendly material, ensuring no release of toxic or harmful gases

Mixing ratio	25kg cement : 6.3L~ 6.5L water
Dry powder density	about 1.3kg\L
Time before covering	about 24-48 hours
Consumption	1.7kg\m \mm2
Compresslve strength	about 6Map after 1 day about 18-20mpa after 28 days
Folding strength	about 2Map after 1 day about 5Map after 28 days
Fire resistance rating	A1