High-Quality Floor Preparation Cement for Wooden Floor Leveling

• Customization: Available
• Application: Commercial Construction, Decorative Concrete, Residential Construction
• Color: Gray
• Model NO.: K20
• Special Additives: Fiber-Reinforced, Shrinkage-Reducing
• Type: High-Strength Concrete
• Mixing Ratio: Cement Vs Water: 25kg Vs 6.3L~ 6.5L
• Dry Powder Density: About 1.3kg\L
• Time Before Covering: About 24-48 Hours
• Consumption: 1.7kg/M2/mm
• Compressive Strength: About 18-20MPa After 28 Days
• Flexural Strength: >5MPa After 28 Days
• Fire Resistance: A1
• Transport Package: Wood Case
• Specification: 25kg/bag
• Trademark: Lan Guan
• Origin: China

Product Description

Product introduction

Lan Guan K20 Self-Leveling Cement for Wooden Flooring is an advanced foundational floor leveling material, meticulously formulated with special cement, premium fine aggregates, polymer spray-dried powder resin sourced from top international brands, and other essential cement additives.

The innovative formula incorporates wood fibers, significantly enhancing the crack resistance of the self-leveling cement, boasting strength levels reaching over 18-20 MPa. This product features remarkable high fluidity and exceptional plasticity, making it the perfect choice for leveling floors in residential wooden flooring applications.

Application scope

Ideal for rapid floor leveling in residential decorations, office spaces, and diverse public areas (such as shopping malls, supermarkets, schools, hospitals, and other bustling public places). The surface is perfectly suited for laying various types of wooden flooring, SPC flooring, carpets, ceramic tiles, stone tiles, and stone slabs. It seamlessly integrates with adhesives for wooden

flooring and adhesives for ceramic tiles and stone materials. The application thickness ranges from 3mm to 40mm. For thicknesses exceeding 40mm, 50% coarse sand aggregate (particle size 3-10mm) should be added. This product is engineered with low shrinkage, ensuring it won't crack or become hollow over time.

 

Performance characteristics

>> High-fluidity material with outstanding self-leveling performance

>> Innovative micro-expansion system, no shrinkage, quick-drying

>> Exceptional crack resistance, applicable thickness ranging from 3mm to 3cm

>> Moisture-proof and resistant to toxicity, extending the

service life of the floor

>> Environmentally friendly composition, no release of toxic or harmful gases

Mixing ratio	25kg cement : 6.3L~ 6.5L water
Dry powder density	about 1.3kg\L
Time before covering	about 24-48 hours
Consumption	1.7kg\m \mm2
Compresslve strength	about 6Map after 1 day about 18-20mpa after 28 days
Folding strength	about 2Map after 1 day about 5Map after 28 days
Fire resistance rating	A1