Durable Wooden Floor Leveler for Efficient Renovation and Repair

• Customization: Available
• Application: Commercial Construction, Decorative Concrete, Residential Construction
• Color: Gray
• Model NO.: K20
• Special Additives: Fiber-Reinforced, Shrinkage-Reducing
• Type: High-Strength Concrete
• Mixing Ratio: Cement Vs Water: 25kg Vs 6.3L~ 6.5L
• Dry Powder Density: About 1.3kg\L
• Time Before Covering: About 24-48 Hours
• Consumption: 1.7kg/M2/mm
• Compressive Strength: About 18-20MPa After 28 Days
• Flexural Strength: >5MPa After 28 Days
• Fire Resistance: A1
• Transport Package: Wood Case
• Specification: 25kg/bag
• Trademark: Lan Guan
• Origin: China

Product Description

Product introduction

Lan Guan K20 Self-Leveling Cement for Wooden Flooring is a premier foundational floor leveling material. Expertly formulated with high-quality special cement, refined aggregates, superior polymer spray-dried powder resin sourced from leading international brands, and other advanced cement additives.

The cutting-edge formula incorporates wood fibers, significantly enhancing the crack resistance of the self-leveling cement, with impressive strength reaching over 18-20 MPa. Boasting exceptional fluidity and high plasticity, it is ideal for leveling floors in residential wooden flooring applications.

Application scope

Perfect for rapid floor leveling in residential decorations, office spaces, and public areas (such as shopping malls, supermarkets, schools, hospitals, and other high-traffic public places). The surface is ideally suited for laying various types of wooden flooring, SPC flooring, carpets, ceramic tiles, stone tiles, and stone slabs. It is compatible with adhesives for wooden

flooring as well as adhesives for ceramic tiles and stone materials. The application thickness ranges from 3mm to 40mm. For thicknesses exceeding 40mm, incorporate 50% coarse sand aggregate (with a particle size of 3-10mm). This product exhibits low shrinkage and ensures a crack-free, non-hollow surface.

 

Performance characteristics

>> High-fluidity material with outstanding self-leveling performance

>> Micro-expansion system, zero shrinkage, rapid drying

>> Exceptional crack resistance, applicable thickness ranging from 3mm to 3cm

>> Moisture-proof and non-toxic, significantly extending the

service life of the floor

>> Environmentally friendly material, no emission of toxic or harmful gases

Mixing ratio	25kg cement : 6.3L~ 6.5L water
Dry powder density	about 1.3kg\L
Time before covering	about 24-48 hours
Consumption	1.7kg\m \mm2
Compresslve strength	about 6Map after 1 day about 18-20mpa after 28 days
Folding strength	about 2Map after 1 day about 5Map after 28 days
Fire resistance rating	A1